EN-GJS-400-15 | 5.3106 Tendency to chilling
| Numeric designation | 5.3106 |
|---|---|
| Chemical designation | EN-GJS-400-15 |
| State | Tendency to chilling |
| Etching | 3 % Nital |
In the perlitic (carbon-rich) region, a ledeburite eutectic (metastable solidification) has formed, the so-called cementitic tendency to chilling. The undesirable formation of tendency to chilling is caused by a too low Si content and too rapid cooling. The mechanical properties determined in the tensile test still look good: Rp0.2: 335 MPa, Rm: 520 MPa, A: 14.0%* (* one sample, very small test cross section).
Cast Iron
GJS-1400-1 | EN-JS1130 | as cast
EN GJSA-XNi35
EN-GJSA-XNiSiCr35-5-2 | 5.3505 | D5S
EN-GJS-500-7 | 5.3200 | Tool life problems in machining
GJS-1400-1 | ADI | Fracture appearance in tensile test
EN-GJS-600-10 | 5.3110 Graphite classification and fracture appearance in tensile tests
EN-GJS-SiMo30-7 | 5.3112 Graphite classification and fracture appearance in tensile test
EN-GJMW-400-5 | Annealing B
GJS-SiMo 40-10 | 5.3115 | Graphite classification and fracture pattern in tensile test
EN-GJMW-400-5 | Annealing A