1.2067 | 102Cr6 +QO +T Hardened and tempered at 150 °C (quenchant: oil)
| Numeric designation | 1.2067 | SAE52100 | AMS6440 |
|---|---|
| Chemical designation | 102Cr6 |
| State | +QO +T Hardened and tempered at 150 °C (quenchant: oil) |
| Etching | 3% Nital |
This hypereutectoid steel (bar stock with ⌀ = 16 mm) was austenitized at 840 °C for 30 min, quenched in oil and then tempered at 150 °C for 2 hours. The microstructure consists of martensite with finely distributed, brightly shining carbides. At low magnification, a slightly network-like structure is still visible.
The core hardness averages 780 ± 4 HV1.
Condition:
840 °C / 30 min / oil – 150 °C / 2 h / air