Back (Additive Manufacturing (AM))

Titanium Grade 23 | Ti6Al4V ELI | PF -45/+15 µm | VED 50 J/mm³ | BUR 9 cm³/h - 08
Titanium Grade 23 | Ti6Al4V ELI | PF -45/+15 µm | VED 50 J/mm³ | BUR 9 cm³/h - 01
Titanium Grade 23 | Ti6Al4V ELI | PF -45/+15 µm | VED 50 J/mm³ | BUR 9 cm³/h - 02
Titanium Grade 23 | Ti6Al4V ELI | PF -45/+15 µm | VED 50 J/mm³ | BUR 9 cm³/h - 03
Titanium Grade 23 | Ti6Al4V ELI | PF -45/+15 µm | VED 50 J/mm³ | BUR 9 cm³/h - 04
Titanium Grade 23 | Ti6Al4V ELI | PF -45/+15 µm | VED 50 J/mm³ | BUR 9 cm³/h - 05
Titanium Grade 23 | Ti6Al4V ELI | PF -45/+15 µm | VED 50 J/mm³ | BUR 9 cm³/h - 06
Titanium Grade 23 | Ti6Al4V ELI | PF -45/+15 µm | VED 50 J/mm³ | BUR 9 cm³/h - 07
Titanium Grade 23 | Ti6Al4V ELI | PF -45/+15 µm | VED 50 J/mm³ | BUR 9 cm³/h - 08
Titanium Grade 23 | Ti6Al4V ELI | PF -45/+15 µm | VED 50 J/mm³ | BUR 9 cm³/h - 09
Titanium Grade 23 | Ti6Al4V ELI | PF -45/+15 µm | VED 50 J/mm³ | BUR 9 cm³/h - 10
Titanium Grade 23 | Ti6Al4V ELI | PF -45/+15 µm | VED 50 J/mm³ | BUR 9 cm³/h - 11

Titanium Grade 23 | Ti6Al4V ELI | PF -45/+15 µm | VED 50 J/mm³ | BUR 9 cm³/h

Numeric designationTitan Grade 23 | 3.7165
Chemical designationTi6Al4V ELI
StateAdditive manufactured by means of L-PBF
EtchingKroll

The microstructure consists of martensite. There are isolated ply bonding defects (~ 200 µm) and blowholes. Etching was done with Kroll for approx. 2 min.

  • Laser class 400 W
  • Beam diameter 80 µm
  • Layer thickness 30 µm
  • VED 50 J/mm³
  • Build-up rate 9 cm³/h
  • Relative density > 99.8
  • Powder grain fraction -45/+15 µm

Additive Manufacturing (AM)