1.0143 | S275J0 Steel beam with fire damage
1.0503 | C45 Incorrect induction hardened
1.0570 | S355J2 Fatigue fracture of a hitch
1.1165 | G28Mn6 with hard facing
1.1191 | C45E crowbar
1.1210 | C53E induction hardened (incorrectly)
1.1248 | C75S HT yes/no
1.2067 | 102Cr6 | SAE52100 | AMS6440 Incomplete martensitic transformation
1.2343 | X37CrMoV5-1 | AISI H11 formation of a hardening crack
1.2343 | X37CrMoV5-1 | AISI H11 thermal fatigue cracks
1.2379 | X153CrMoV12 built-up welding with crack
1.2379 | X153CrMoV12 Forging defect
1.2379 | X153CrMoV12 with crack
1.2379 | X153CrMoV12 with crack in the HAZ
1.4021 | X20Cr13 gas-nitrided, fatigue fracture
1.4462 | X2CrNiMoN22-5-3 Duplex with sigma phase
1.4571 | X6CrNiMoTi17-12-2 Fatigue Corrosion Cracking
1.4740 mod | GX40CrSi17 Immersion pipe from the cement industry
1.4765 | X8CrAl25-5 AlN precipitations
1.4823 | GX40CrNiSi27-4 Centre line shrinkage cavity
1.4832 | GX25CrNiSi20-14 Dipstick for molten zinc
1.4837 | GX40CrNiSi25-12 Hot corrosion with molten sulfate
1.4849 | GX40NiCrSiNb38-19 Magnetism in charging racks
1.4938 | X12CrNiMoV12-3 carbide inclusions
1.6565 | 40NiCrMo6 Broken shaft of an impact hammer mill
1.6568 | 30CrNiMo5-5 broken shaft
1.6580 | 30CrNiMo8 +N + QT Forging crack
1.6759 | G18NiMoCr3-6 fisheye, hydrogen embrittlement
1.7131 | 16MnCr5 | AISI 5115 Forging lap in case-hardened bushing
1.7225 | 42CrMo4 Quasi-gap fracture
2.4879 | G-NiCr28W Fracture of a Furnace Roll
AC-46000 | AlSi9Cu3(Fe) Fatigue fracture in sand casting
Al extruded profile with alleged extrusion defect
Breakage of a side cutter
CC499K | CuSn5Zn5Pb2-C Brass fitting with hot crack
Chisel, fracture
CuAl8 solder on S235JR, liquid metal induced stress corrosion cracking
Ductile overload fracture of a steel pipe with “tire tracks”
EN AC-42200 | AlSi7Mg0,6 Fatigue fracture vs. overload fracture
EN AC-43000 | AlSi10Mg die casting, Cold flow marks
EN AC-43500 | AlSi10MnMg Cold run and hot crack
EN AC-46000 | AlSi9Cu3 non-refined sand casting
EN AW-2007 | AlCu4PbMg | AA2007 Cracks due to cumulative and coarse precipitations
EN AW-7075 | AlZn5,5MgCu1,5 Fatigue Corrosion Cracking
EN-GJL-200 | 5.1300 Overload fracture in gray cast iron
EN-GJS-500-7 | 5.3200 | Tool life problems in machining
Fatigue fracture of a garden tool
Fatigue fracture of an osteosynthesis plate
Graphite degeneration: White irradiation in GJS | Damage case with brittle cleavage fracture
Hydrogen embrittlement in locking washer
Manufacturing error on a feather
Material bulge in rolled screw 12.9
Oven heating coil
Pastry tong, fracture | silver alloy
Screw with heat treatment defect
SD40 Reinforcing ribbed steel | C=0.25%
WEA White Etching Area
Wire rope friction martensite
ZL0410 | ZnAl4Cu1 Broken zinc die-cast snap hook
ZL0410 | ZnAl4Cu1 Overload fractur of a bottle opener