Titan Grade 23 | Ti6Al4V ELI | PF -45/+15 µm | VED 117 J/mm³ | BUR 11 cm³/h - 04
Titan Grade 23 | Ti6Al4V ELI | PF -45/+15 µm | VED 117 J/mm³ | BUR 11 cm³/h - 01
Titan Grade 23 | Ti6Al4V ELI | PF -45/+15 µm | VED 117 J/mm³ | BUR 11 cm³/h - 02
Titan Grade 23 | Ti6Al4V ELI | PF -45/+15 µm | VED 117 J/mm³ | BUR 11 cm³/h - 03
Titan Grade 23 | Ti6Al4V ELI | PF -45/+15 µm | VED 117 J/mm³ | BUR 11 cm³/h - 04
Titan Grade 23 | Ti6Al4V ELI | PF -45/+15 µm | VED 117 J/mm³ | BUR 11 cm³/h - 05
Titan Grade 23 | Ti6Al4V ELI | PF -45/+15 µm | VED 117 J/mm³ | BUR 11 cm³/h - 06
Titan Grade 23 | Ti6Al4V ELI | PF -45/+15 µm | VED 117 J/mm³ | BUR 11 cm³/h - 07
Titan Grade 23 | Ti6Al4V ELI | PF -45/+15 µm | VED 117 J/mm³ | BUR 11 cm³/h - 08
Titan Grade 23 | Ti6Al4V ELI | PF -45/+15 µm | VED 117 J/mm³ | BUR 11 cm³/h - 09
Titan Grade 23 | Ti6Al4V ELI | PF -45/+15 µm | VED 117 J/mm³ | BUR 11 cm³/h - 10
Titan Grade 23 | Ti6Al4V ELI | PF -45/+15 µm | VED 117 J/mm³ | BUR 11 cm³/h - 11
Titan Grade 23 | Ti6Al4V ELI | PF -45/+15 µm | VED 117 J/mm³ | BUR 11 cm³/h - 12
Titan Grade 23 | Ti6Al4V ELI | PF -45/+15 µm | VED 117 J/mm³ | BUR 11 cm³/h - 13

Titan Grade 23 | Ti6Al4V ELI | PF -45/+15 µm | VED 117 J/mm³ | BUR 11 cm³/h

Numerische BezeichnungTitan Grade 23 | 3.7165
Chemische BezeichnungTi6Al4V ELI
ZustandAdditiv gefertigt mittels L-PBF
ÄtzungKroll

Bei der raschen Abkühlung wandelt das beta-Gefüge direkt in nadeligen Martensit um. Lokal gibt es Lagenbindefehler (~ 150 µm) und Poren (~ 40 µm). Geätzt wurde mit Kroll ca. 2 min.

  • Laserklasse 400 W
  • Strahldurchmesser 130 µm
  • Schichtdicke 30 µm
  • VED 117 J/mm³
  • Aufbaurate 11 cm³/h
  • Relative Dichte > 99.8 %
  • Pulverkornfraktion -45/+15 µm

Additive Fertigung (AM)

Kategorie anzeigen