Titan Grade 23 | Ti6Al4V ELI | PF -45/+15 µm | VED 58 J/mm³ | BUR 21,6 cm³/h - 03
Titan Grade 23 | Ti6Al4V ELI | PF -45/+15 µm | VED 58 J/mm³ | BUR 21,6 cm³/h - 01
Titan Grade 23 | Ti6Al4V ELI | PF -45/+15 µm | VED 58 J/mm³ | BUR 21,6 cm³/h - 02
Titan Grade 23 | Ti6Al4V ELI | PF -45/+15 µm | VED 58 J/mm³ | BUR 21,6 cm³/h - 03
Titan Grade 23 | Ti6Al4V ELI | PF -45/+15 µm | VED 58 J/mm³ | BUR 21,6 cm³/h - 04
Titan Grade 23 | Ti6Al4V ELI | PF -45/+15 µm | VED 58 J/mm³ | BUR 21,6 cm³/h - 05
Titan Grade 23 | Ti6Al4V ELI | PF -45/+15 µm | VED 58 J/mm³ | BUR 21,6 cm³/h - 06
Titan Grade 23 | Ti6Al4V ELI | PF -45/+15 µm | VED 58 J/mm³ | BUR 21,6 cm³/h - 07
Titan Grade 23 | Ti6Al4V ELI | PF -45/+15 µm | VED 58 J/mm³ | BUR 21,6 cm³/h - 08
Titan Grade 23 | Ti6Al4V ELI | PF -45/+15 µm | VED 58 J/mm³ | BUR 21,6 cm³/h - 09
Titan Grade 23 | Ti6Al4V ELI | PF -45/+15 µm | VED 58 J/mm³ | BUR 21,6 cm³/h - 10
Titan Grade 23 | Ti6Al4V ELI | PF -45/+15 µm | VED 58 J/mm³ | BUR 21,6 cm³/h - 11
Titan Grade 23 | Ti6Al4V ELI | PF -45/+15 µm | VED 58 J/mm³ | BUR 21,6 cm³/h - 12
Titan Grade 23 | Ti6Al4V ELI | PF -45/+15 µm | VED 58 J/mm³ | BUR 21,6 cm³/h - 13

Titan Grade 23 | Ti6Al4V ELI | PF -45/+15 µm | VED 58 J/mm³ | BUR 21,6 cm³/h

Numerische BezeichnungTitan Grade 23 | 3.7165
Chemische BezeichnungTi6Al4V ELI
ZustandAdditiv gefertigt mittels L-PBF
ÄtzungKroll

Das Gefüge besteht aus Martensit. Es gibt Lagenbindefehler (~ 200 µm), die sich über mehrere Lagen erstrecken sowie Poren. Bei dieser hohen Aufbaurate liegen noch nicht vollständig aufgeschmolzene Pulverpartikel vor. Geätzt wurde mit Kroll ca. 2 min.

  • Laserklasse 400 W
  • Strahldurchmesser 130 µm
  • Schichtdicke 30 µm
  • VED 58 J/mm³
  • Aufbaurate 21,60 cm³/h
  • Relative Dichte > 99.8 %
  • Pulverkornfraktion -45/+15 µm

Additive Fertigung (AM)